Zaštita materijala
2020, vol. 61, br. 1, str. 52-59
jezik rada: engleski
vrsta rada: naučni članak
objavljeno: 27/03/2020
doi: 10.5937/zasmat2001052M
Creative Commons License 4.0
Mehanička i mikrostrukturna svojstva VPS-Ti porozne prevlake deponovane na podlogama od legure titana za osteointegraciju
aUniverzitet u Beogradu, Tehnološko-metalurški fakultet
bUniverzitet u Beogradu, Poljoprivredni fakultet
cUniverzitet u Beogradu, Tehnološko-metalurški fakultet, Inovacioni centar
dUniversity of Montenegro, Faculty of Mechanical Engineering, R. Montenegro

e-adresa: drmrdakmihailo@gmail.com

Projekat

Mikromehanički kriterijumi oštećenja i loma (MPNTR - 174004)
Razvoj tehnologije izrade obloge i jezgra na bazi domaćih sirovina za proizvodnju specijalnih obloženih elektroda namenjenih za elektrolučno zavarivanje čelika (MPNTR - 34016)

Sažetak

Topografija površine deponovanih VPS-Ti prevlaka na podlogama implanata koja se odnosi na hrapavost i poroznu strukturu imaju odlučujuću ulogu u procesu srastanja implanata sa kostima odnosno osteointegraciju Direktno urastanje kostiju uspešno se posti e korišćenjem mikro grubih površina prevlaka, kao što je primena vakuum plazma sprej VPS - Ti prevlake. Cilj ovog rada je bio da se napravi sveobuhvatan pregled karakterizacija VPS-Ti poroznih prevlaka deponovanih na podlogama od legure titana koje će naći aplikaciju u ortopediji. Jedna od povoljnih osobina VPS procesa je mogućnost postizanja optimalne makro i mikro strukture površine implanata optimizacijom sprej parametara depozicije praha i rasponom granulacije praha. U cilju postizanja optimalne hrapavosti, otvorene poroznosti i strukture VPS-Ti prevlaka sprovedena je optimizacija depozicije praha sa promenom plazma struje i protokom nosećeg gasa praha (700 A, 35 l/min i 800A, 20 l/min) Ni a jačina plazma struje uz veći protok praha slabije progreva i topi čestice praha obrazujući mikro pore veće veličine i veći udeo otvorenih pora i obrnuto veća plazma struja i manji protok omogućuju bolje topljenje čestica uz formiranje manjeg udela mikro pora i otvorene poroznosti u deponovanim slojevima. Analizom slika ustanovljeno je da se sa optimizacijom parametara u prevlakama mo e formirati otvorena poroznost sa rasponom od 45% do 57% Ispitivanjem karakteristika deponovanih slojeva ustanovljeno je da najoptimalniju hrapavost i udeo otvorenih pora za osteointegraciju imaju slojevi Ti deponovani sa najni om ampera om i najvećim protokom nosećeg gasa praha.

Ključne reči

osteointegracija; VPS-Ti; poroznost; čvrstoća spoja; mikrostruktura

Reference

*** (2009) ASTM F1854: Standard test method for stereological evaluation of porous coating on medical implants. West Conshohocken, PA: ASTM International
*** (1994) ASMI handbook: Materials properties handbook: Titanium alloys
*** (2008) ASTM C633-1(2008) standard test method for adhesion or cohesion strength of thermal spray coatings. Reapproved
Altankov, G., Grinnell, F., Groth, T. (1996) Studies on the biocompatibility of materials: Fibroblast reorganization of substratum-bound fibronectin on surfaces varying in wettability. Journal of Biomedical Materials Research, 30(3), 385-391
Bose, S., Roy, M., Bandyopadhyay, A. (2012) Recent advances in bone tissue engineering scaffolds. Trends in Biotechnology, 30(10), 546-554
Chen, S., Jones, J.A., Xu, Y., Low, H.Y., Anderson, J.M., Leong, K.W. (2010) Characterization of topographical effects on macrophage behavior in a foreign body response model. Biomaterials, 31(13), 3479-3491
Fabi, D.W., Levine, B.R. (2012) Porous coatings on metallic implant materials. u: ASM Handbook, Volume 23: Materials for Medical Devices, ASM International, p.307-319
Mariani, E., Lisignoli, G., Borzì, R.M., Pulsatelli, L. (2019) Biomaterials: Foreign bodies or tuners for the immune response?. International Journal of Molecular Sciences, 20(3). 636-636
Metco, O. (2017) Material product data sheet, pure titanium and titanium alloy powders thermal spray powders. DSMTS-0089.5
Mrdak, M., Bajić, N., Veljić, D., Rakin, M., Pekez, J., Karastojković, Z. (2016) Testing adhesive bond strength and fracture mechanisms of thicker and porous plasma spray coatings. u: VI International Conference Industrial Engineering and Environmental Protection 2016 (IIZS 2016), Zrenjanin: University of Novi Sad, Technical faculty 'Mihajlo Pupin, 249-253
Mrdak, M., Lačnjevac, Č., Rakin, M. (2018) Mechanical and structural features of Nb coating layers deposited on steel substrates in a vacuum chamber. Zaštita materijala, vol. 59, br. 2, str. 167-172
Mrdak, M., Lačnjevac, Č., Rakin, M., Bajić, N. (2018) Characterization of tantalum coatings deposited using vacuum plasma spray process. Zaštita materijala, vol. 59, br. 4, str. 489-494
Mrdak, M., Lačnjevac, Č., Rakin, M., Bajić, N., Veljić, D. (2019) Karakterizacija plazma sprej bioinertne prevlake Al2O328tež.%MgO. Zaštita materijala, vol. 60, br. 1, str. 44-49
Wertz, C.F., Santore, M.M. (2001) Santore effect of surface hydrophobicity on adsorption and relaxation of kinetics of albumin and fibrinogen: Single-species and cpmpetitive behaviour. Langmuir, 17(10), 3006-3016
Winkler-Gniewek, W. (1989) Die Plasmapore-Beschichtung für die zementlose Verankerung von Gelenkendoprothesen. u: Wissenschaftliche Informationen, Vormals Jetter und Scheerer (Tuttlingen), Tom 22