2011, vol. 61, br. 3-4, str. 73-77
|
|
Mokronamotane kompozitne plastične cevi - odnos između strukture namotavanja i hidrauličkih i mehaničkih osobina
Filament wound composite plastic tubes: Relationship between winding structures and their hydraulic and mechanical properties
Vojnotehnički institut - VTI, Beograd
Sažetak
Struktura namotavanja označava broj slojeva i uglove pod kojim se namotava vlaknasto ojačanje, u odnosu na uzdužnu osu cevi. Cevi četiri različite strukture namotavanja urađene su tehnologijom mokrog namotavanja staklenog rovinga impregnisanog sistemom poliestarske smole. Epruvete cevi za hidrauličko testiranje i uzorci prstenova za mehanička ispitivanja dobijeni su mašinskom obradom mokronamotanih cevi. Epruvete cevi četiri različite strukture namotavanja izložene su dejstvu unutrašnjeg hidrauličkog pritiska fluida i određene su vrednosti pritiska prskanja, radijalnih deformacija i promene poluprečnika. Uzorci prstenova su ispitani pod dejstvom zateznog opterećenja i određena je prekidna čvrstoća. Zaključeno je da struktura ima bitan uticaj na hidrauličke i mehaničke karakteristike mokronamotanih kompozitnih plastičnih cevi.
Abstract
A winding structure denotes the number of layers and the winding angle at which a reinforcing fiber is wound. regarding the tube longitudinal axis. Tubes with four different winding structures were produced by the filament winding technology of glass roving impregnated by a polyester resin system. Test tubes for hydraulic testing and ring specimens for mechanical investigation were produced by machining. Test tubes with four different winding structures were exposed to the influence of internal fluid hydraulic pressure. The burst pressure, radial deformation and radius displacement were determined. The ring specimens were exposed to tensile stress and their ultimate strength was determined. It is concluded that the winding structure has the essential influence on the hydraulic and mechanical properties of filament wound composite plastic tubes.
|
|
|
|
Reference
|
|
|
*** ASTM D 2290 apparent tensile strength of parallel reinforced plastic materials by split ring method. Philadelphia: ASTM Committee of Standards
|
|
10  
|
Ashby, M.F. (1999) Materials selection in mechanical design. Oxford: Butterworth Heinemann
|
|
5
|
Kelly, A. (1989) CONCISE encyclopedia of composite materials. Oxford: Pergamon Press
|
|
6  
|
Radulović, J. (2008) Karakterizacija mokronamotanih polimernih kompozitnih materijala. Scientific Technical Review, vol. 58, br. 1, str. 66-75
|
|
2
|
Radulović, J. (2010) Uticaj cikličnog unutrašnjeg pritiska na kvalitet mokronamotanih kompozitnih cevi. Scientific Technical Review, vol. 60, br. 1, str. 54-60
|
|
|
|
|